The bauxite residue (BR) is the solid waste of largest generation by the aluminum industry, with a generation estimated in 10 million ton/year in Brazil. Its high alkalinity demands elevated costs to store it safely. Due to the high content of Al2O3 and Fe2O3 in BR, the present study evaluated its application for the synthesis of iron rich sulfobelite clinkers. Because of its composition, the cement made with this clinker presents environmental (30% to 62% reduction of CO2-equivalent emission), economic and even technical advantages over Portland cements. Formulations containing: limestone, gypsum, BR and clay, were fired at 1230°C to synthesize the clinkers. Variations in BR and clay content were studied to obtain three formulations, F-15, F-18 and F-21, of different Al2O3/Fe2O3 ratio values. Cements containing more than 10.5 wt-% of BR achieved mechanical resistance comparable to Portland cements (CP-II-Z32 and CP-V-ARI) for 7 and 28 days of curing age.

Calcium aluminate cements (CAC) were prepared using the sonochemical process, followed by heat treatment. A study was made of the action of ultrasonic waves and the influence of thermal treatment conditions on two initial molar compositions of 1:1 and 1:2 of calcia:alumina. The aqueous suspension containing the raw materials (A-50 alumina and CaO) was subjected to an ultrasonic bath, followed by drying and burning at 1000, 1200 and 1300 ºC. These cements were characterized by SEM, XRD and the mechanical strength was evaluated by splitting tensile tests, using commercial cement as a reference. Furthermore, the phases were semi-quantified using the Rietveld method. The results show that hydration and sonochemical action increased the reactivity of the raw materials during firing and that phase formation is dependent on the thermal treatment conditions. The CAC cements were obtained at temperatures at least 200 ºC lower than those used in conventional methods, indicating the potential of this route of synthesis.